● Materiaalvorm: korrelig
● Verwerkingsmethode: spuitgieten
● Vlamvertragende klasse: HB
● Materiaaleigenschappen: 20% glasvezelversterkt
● Naleving: UL
● Material characteristics: dimensional stability, low shrinkage, good mechanical properties, low warpage
● Material use: axial flow fan, centrifugal fan, cross-flow fan, injection molding application
| Materiaal Technisch gegevensblad | ||||
| AS G4 K01 | ||||
| EIGENDOM | ||||
| 20% glasvezelversterkt | ||||
| KENMERKEN | Toepassingen | |||
| Dimensionale stabiliteit | Axiale fans | |||
| Lage krimp | Centrifugaal fans | |||
| Goede mechanische eigenschappen | Cross flow fans | |||
| Lage kromming | Spuitgiettoepassingen | |||
| Aanbod | Test standaard | Test conditie | Eenheden | Typische waarden |
| Fysieke eigenschappen | ||||
| Soortelijk gewicht 23°C | ISO 1183 | 23 ℃ | g / cm³ | 1.22 |
| Krimpsnelheid Stroom 23°C | ISO 2577 | 23 ℃ | % | 0.1 0.3 ~ |
| Smeltindex 230°C 5kg | ISO 1133 | 23 ℃ | % | 15 |
| Mechanische eigenschappen | ||||
| Mechanische eigenschappen | Test standaard | Test conditie | Eenheden | Data |
| Treksterkte 10 mm/min | ISO 527 | 10mm / min | Mpa | 115 |
| Rek bij breuk 10 mm/min | ISO 527 | 10mm / min | % | 2 |
| Flexural Strength2.0mm/min | ISO 178 | 2.0mm / min | Mpa | 155 |
| Buigmodulus 2.0 mm/min | ISO 178 | 2.0mm / min | Mpa | 7100 |
| Cantilever-inkeping impact 23°C | ISO 180 | 23 ° C A-stand | kJ/m² | 6.5 |
| Thermische eigenschappen | ||||
| Thermische eigenschappen | Test standaard | Test conditie | Eenheden | Data |
| Thermische vervormingstemperatuur | ISO 75 | 0.45MPa | ℃ | 102 |
| Vica-verwekingstemperatuur | ISO 306 | 1.8MPa | ℃ | 112 |
| Elektrische prestaties | ||||
| Elektrische prestaties | Test standaard | Data | Eenheden | |
| Volumeweerstand | IEC 60093 | 1E16 | Ω.cm | |
| Isolatiesterkte 2.0 mm in olie | IEC 60243 | 23 | KV / mm | |
| Vlamvertraging | ||||
| Vlamvertraging | Test standaard | Data | ||
| Fire Rating Full Color black 1.6mm | UL94 | HB | ||
| Fire Rating Full Color black 3.2mm | UL94 | HB | ||
| UL | ||||
| Vlamvertraging | Test standaard | Data | Eenheden | |
| Fire Rating Full Color black 1.6mm | UL94 | HB | ||
| Fire Rating Full Color black 3.2mm | UL94 | HB | ||
| RTI Elec Full color black 1.6mm | UL 746B | 50 | ° C | |
| RTI Elec Full color black 3.2mm | UL 746B | 50 | ° C | |
| RTI Imp Full color black 1.6mm | UL 746B | 50 | ° C | |
| RTI Imp Full color black 3.2mm | UL 746B | 50 | ° C | |
| RTI Str Full color black 1.6mm | UL 746B | 50 | ° C | |
| RTI Str Full color black 3.2mm | UL 746B | 50 | ° C | |
| Injection Molding | ||||
| Injection Molding | Eenheden | Data | ||
| Droogtemperatuur | ℃ | 80 90 ~ | ||
| Droog tijd | hr | 2 4 ~ | ||
| Temperatuur voorzijde | ℃ | 190 215 ~ | ||
| Middelmatige temperatuur | ℃ | 210 250 ~ | ||
| Temperatuur van de derde sectie | ℃ | 220 260 ~ | ||
| Smelttemperatuur | ℃ | 210 250 ~ | ||
| Maximale smelttemperatuur | ℃ | 260 | ||
| Vormtemperatuur | ℃ | 40 90 ~ | ||
| Injectiesnelheid | Lage tot gemiddelde snelheid | |||
| Tegendruk | KPa | 0.0 1000 ~ | ||
Flame retardant grade :HB/ Material properties: 10% glass fiber reinforced
Meer lezen
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. Alle rechten voorbehouden.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ